Pregunta 1
Pregunta
1. When making repairs to stainless-steel overlay on carbon steel base material, the repair shall be inspected by ?
Respuesta
-
A. Radiographic testing
-
B. Penetrant testing
-
C. Ultrasonic examination
-
D. Penetrant and ultrasonic testing
Pregunta 2
Pregunta
2. Temper embrittlement is a metallurgical change that is ?
Respuesta
-
A. Not readily apparent but can be confirmed through tension testing
-
B. Readily apparent and can be confirmed through impact testing
-
C. Readily apparent and can be confirmed through metallography
-
D. Not readily apparent but can be confirmed through impact testing
Pregunta 3
Pregunta
3. Non – normalized SA 516 Gr 60 material is used for fabricating a pressure vessel that has a nominal wall thickness of 1.125 inches (28.6mm). What is the minimum design metal temperature for the vessel that does not require impact testing ?
Respuesta
-
A. - 26˚F (-32˚C)
-
B. 2˚F (-17˚C)
-
C. 37˚F (3˚C)
-
D. 75˚F (24˚C)
Pregunta 4
Pregunta
4. When reviewing a group of radiographs, all following information must be documented except ?
Respuesta
-
A. Source to object distance
-
B. Geometric un sharpness
-
C. Material type
-
D. Single or double wall exposure
Pregunta 5
Pregunta
5. If a repair is made on a pressure vessel using a filler metal with lower specified minimum tensile strength than base metal, all of the following requirement apply except ?
Respuesta
-
A. The repair shall be made with minimum of two passes
-
B. The increased thickness of the repair shall have rounded corners and blend into the base metal using a 3 : 1 taper
-
C. A minimum preheat of 175 Deg F (79.4 Deg C) and an inter pass temperature of 450 Deg F (232Deg C)must be maintained
-
D. The repair thickness shall not more than 50 % of the required base metal thickness excluding corrosion allowance